Product Description:
HY326 anaerobic adhesive is a single component adhesive solution that can fully fill the gaps in the fit, does not shrink during curing, has good medium resistance, high bonding strength, and high impact resistance. Suitable for bonding hard materials such as metal, glass, porcelain, ferrite, etc.
Curing mechanism:
Anaerobic adhesive solidifies by isolating oxygen and reacting with metal ions. The more lively the adhered metal, the higher the ambient temperature, and the smaller the bonding gap, the faster the curing process. Non metallic materials and inert metal materials must use anaerobic adhesive accelerators.
Product curing characteristics:
The relationship between curing speed and substrate
The curing speed mainly depends on the substrate used, and the comparison test of the relationship between shear strength and curing time is shown in the figure.
nine hundred and two thousand nine hundred and three
The relationship between curing speed and temperature
The curing speed also depends on the temperature, shear strength, curing time, and testing at different temperatures, as shown in the following figure:
nine hundred and two thousand nine hundred and five
The relationship between curing speed and gap
The curing speed also depends on the size of the gap, as shown in the following figure, which shows the curing speed at different gaps:
nine hundred and six
nine hundred and seven
The relationship between curing speed and accelerator
When the material is not metal or the metal surface is inert metal with large gaps, accelerator HY764 should be used to accelerate curing, as shown in Figure HY326 for the failure strength of HY764 accelerator on chrome plated materials and metal sleeves.
Chemical resistant medium:
  This product can withstand fresh water, sewage, wastewater, calcium carbonate aqueous solution, cleaning agents, low acidity, corrosive aqueous solution, etc. for a long time. It is resistant to oil products such as engine oil, lubricating oil, gasoline, ethanol, etc. It is not resistant to organic solvents, high concentrations of acid and alkali, etc.
usage method:
1. Clean the mating surface with HY755 cleaning agent.
2. Apply the adhesive onto the mating surface, rub left and right slowly, and remove excess adhesive.
3. Curing at 25 ℃ for 1 hour can withstand small shear forces.
4. When the gap is large, measures should be taken to spray the accelerator.
5. When traditional methods cannot disassemble, it can be locally heated to above 230 ℃ and pulled out while still hot.
matters needing attention:
♦ Unused products should be sealed and stored to prevent impurities such as metal ions from mixing into the adhesive solution
♦ Winter temperatures are low, causing the glue to thicken without affecting its performance
♦ For special chemical reactions, please contact our technical department
Packaging specifications:
50ml/bottle, 250ml/bottle
Storage method:
Store in a cool and dry place, with a shelf life of one year.
Safety and hygiene:
This product has no toxic effects and is the same as general chemicals. It cannot come into contact with food or food utensils. It is recommended to maintain sufficient ventilation in the work environment. In case of entering the eyes or mouth, rinse immediately with water. Store in a safe place, away from children.
Declaration:
The technical parameters mentioned in this article are typical values and are not used as product acceptance criteria. They are for reference only. The above data was obtained under standard laboratory conditions, and our company guarantees its reliability. However, due to different working conditions used by users, different surface states of materials, and different curing conditions, some changes in actual performance data are normal phenomena. Storage conditions, transportation, and other factors can all affect the stability, physical and mechanical properties of the adhesive. We are not responsible for any results obtained by anyone using methods beyond our control. It is recommended that users conduct experiments based on the data provided in this article before formal use.